Acceleration sensor and process for the production thereof
RE41047 Acceleration sensor and process for the production thereof
Patent Drawings:Drawing: RE41047-10    Drawing: RE41047-11    Drawing: RE41047-12    Drawing: RE41047-13    Drawing: RE41047-14    Drawing: RE41047-15    Drawing: RE41047-16    Drawing: RE41047-3    Drawing: RE41047-4    Drawing: RE41047-5    
« 1 2 »

(14 images)

Inventor: Fujii
Date Issued: December 22, 2009
Application: 10/315,566
Filed: December 10, 2002
Inventors: Fujii; Tetsuo (Kariya, JP)
Assignee: Denso Corporation (Kariya, JP)
Primary Examiner: Kwok; Helen C.
Assistant Examiner:
Attorney Or Agent: Harness, Dickey & Pierce, PLC
U.S. Class: 73/514.18; 73/514.32; 73/514.36
Field Of Search: 73/514.18; 73/514.32; 73/514.36; 73/514.16; 73/514.29; 73/514.17
International Class: G01P 15/125
U.S Patent Documents:
Foreign Patent Documents: 2 240 178; 2 246 635; 59-44875; 60-29629; 60-244864; 61-73071; 62-27666; 62-93668; 62-174978; 62-207917; 62-232171; 63-25982; 63-250865; 2-237 166; 2-309259; 3-94168; 3-205565; 4-76956; 404076956; 6-88837; 6-173071; 6-227666; 8-510837; 91/12497
Other References: "Fabrication Technologies For Integrated Microdynamic Systems", W. Yun, W.C. Tang and R.T. Howe, Presented at the Third Toyota Conference,Aichi-ken, Japan: Oct. 22-25, 1989. cited by other.
"Novel Process for a Monolithic Integrated Accelerometer", M. Offenberg, F. Larmer, B. Eisner, H. Munzel and W. Riethmuller, The 8th International Conference on Solid-State Sensors and Actuators, and Eurosensors IX, Stockholm, Sweden, Jun. 25-29,1995. cited by other.
Office Action issued by Japanese Patent Office Action on Oct. 23, 2001 in connection with Priority Application No. JP-4-108020 and citing various ones of above references. cited by other.
Payne et al., "Surface Micromachined Accelerometer: A Technology Update," SAE Technical Paper Series, Feb. 25, 1991, pp. 127-135. cited by other.









Abstract: A single crystal silicon substrate (1) is bonded through an SiO.sub.2 film (9) to a single crystal silicon substrate (8), and the single crystal silicon substrate (1) is made into a thin film. A cantilever (13) is formed on the single crystal silicon substrate (1), and the thickness of the cantilever (13) in a direction parallel to the surface of the single crystal silicon substrate (1) is made smaller than the thickness of the cantilever in the direction of the depth of the single crystal silicon substrate (1), and movable in a direction parallel to the substrate surface. In addition, the surface of the cantilever (13) and the part of the single crystal silicon substrate (1), opposing the cantilever (13), are, respectively, coated with an SiO.sub.2 film (5), so that an electrode short circuit is prevented in a capacity-type sensor. In addition, a signal-processing circuit (10) is formed on the single crystal silicon substrate (1), so that signal processing is performed as the cantilever (13) moves.
Claim: I claim:

.[.1. An acceleration sensor comprising: a first substrate formed of a silicon material which is used as a conductive material; a second substrate provided on the lower side of saidfirst substrate and electrically insulated from the first substrate; said first substrate including: a support beam having a mass portion forming capacitive electrodes for displacement in a parallel direction to a surface of said second substrateaccording to the degree of acceleration, a fixed portion for fixing said support beam to said second substrate and a support portion for intermediately supporting said mass portion to said fixed portion, an insulating groove extending through a thicknessof said first substrate around the entire periphery of said support beam, and stationary blocks forming capacitive electrodes defined by said insulating groove on the outer sides of said support beam separately across said insulating groove and fixed tosaid second substrate; and gap means forming a gap space in order to space said mass portion and said supporting portion from a surface of said second substrate; and said second substrate being separated from said first substrate by an insulating layerwhich is at least provided on the lower side of said fixed portion and stationary blocks..].

.[.2. An acceleration sensor as defined in claim 1, wherein said insulating groove defines a narrow detection groove between said mass portion of said support beam and each of said stationary blocks, and movable and stationary electrodes areformed on lateral side surfaces of said support beam and said stationary blocks in face to face relation with each other across said detection groove..].

.[.3. An acceleration sensor as defined in claim 1, wherein said support beam is securely fixed to said second substrate at said fixed end, and reduced in a width in said support portion to provide at least one support for said mass portion ina fore free end portion to be displayed horizontally according to the degree of acceleration in the fashion of at least one fulcrum point type acceleration sensor..].

.[.4. An acceleration sensor as defined in claim 3, wherein said width of said support portion is smaller than a thickness of said fixed portion and said support beam provides a cantilever type support..].

.[.5. An acceleration sensor as defined in claim 1, wherein said first substrate is formed of silicon material with a (100) crystal face..].

.[.6. An acceleration sensor as defined in claim 5, wherein said first substrate is formed of a n-type silicon material..].

.[.7. An acceleration sensor as defined in claim 1, wherein said second substrate is formed of a silicon material having a surface covered with an insulating oxidation film..].

.[.8. An acceleration sensor comprising: a substrate which is selected from the group consisting of an insulating material and oxidized semiconductor material; a support beam which includes a mass portion forming a predetermined mass and firstcapacitive electrodes on side surfaces of said mass portion, a fixed portion for fixing said support beam to said substrate and a thin support portion for intermediately connecting between said mass portion and said fixed portion; a pair of stationaryblocks arranged on both sides of said support beam separately across an air gap and fixed to said substrate, said stationary blocks provided with second capacitive electrodes on the opposite sides of first capacitive electrodes of said mass portion; gapmeans forming a gap space in order to space said mass portion and thin support portion from a surface of said substrate; and said mass portion being displace in a parallel direction to the surface of said substrate according to the degree ofacceleration and said support beam and stationary blocks formed of a silicon material which is used as a conductive material and electrically insulated from said substrate..].

.[.9. An acceleration sensor as defined in claim 8, wherein said gap means is formed of an insulating layer at least between said substrate and said fixed portion of the support beam and said stationary blocks..].

.[.10. An acceleration sensor as defined in claim 8, wherein movable and stationary electrodes are formed on lateral side surfaces of said mass portion and said stationary blocks in face to face relation with each other across said air gap..].

.[.11. An acceleration sensor as defined in claim 8, wherein a width of said thin support portion is smaller than a thickness of said fixed portion..].

.[.12. An acceleration sensor as defined in claim 8, wherein said support beam and stationary blocks are formed of a n-type silicon material with a (100) crystal face..].

.[.13. An acceleration sensor as defined in claim 8, wherein said substrate is formed of a silicon material having a surface covered with an insulating oxidation film..].

.[.14. An acceleration sensor comprising: A. a first single crystalline silicon substrate having a first surface and a second surface opposite said first surface; B. a second single crystalline silicon substrate connected to a side of saidfirst surface of said first single crystalline silicon substrate with an insulating layer interposed therebetween; C. said first single crystalline silicon substrate including; i. a movable beam defined by a trench which is disposed to surround saidmovable beam and extend from said second surface to said first surface, said movable beam being supported by said second single crystalline silicon substrate through said insulating layer to be displaceable in a direction parallel to said first surfaceof said first single crystalline silicon substrate, ii. a stationary block disposed to be spaced apart from said movable beam via said trench, facing said movable beam to form a pair of capacitive electrodes with said movable beam, and fixed to saidsecond single crystalline silicon substrate; and D. a signal-processing circuit element for carrying out a processing operation based on a change of a capacitance between said capacitive electrodes..].

.[.15. An acceleration sensor according to claim 14, wherein said movable beam has a first thickness along said direction parallel to said first surface of said first single crystal silicon substrate and a second thickness in a directionperpendicular to said first surface of said first crystal silicon substrate, said first thickness being smaller than said second thickness..].

.[.16. An acceleration sensor according to claim 14, wherein at least one of a surface of said movable beam exposed to said trench and a surface of said first single crystal silicon substrate facing said movable beam is covered with aninsulator..].

.[.17. An acceleration sensor according to claim 14, wherein said movable beam or said stationary block comprise an impurity-doped region to form said capacitive electrodes..].

.[.18. An acceleration sensor according to claim 14, further comprising first, second and third stationary blocks, each of which is formed of a part of said first single crystal silicon substrate, and wherein said movable beam includes a firstbranch and a second branch, said first branch being interposed between said stationary block and said first stationary block with a first air gap defined therebetween, said second branch of said movable beam being interposed between said second and saidthird stationery blocks with a second air gap defined therebetween, said stationary block and said second stationary block being electrically connected with each other, said first and said third stationary blocks being electrically connected with eachother..].

.[.19. An acceleration sensor according to claim 14, wherein said signal-processing circuit is disposed on said first single crystal silicon substrate..].

.[.20. An acceleration sensor comprising: A. a first single crystalline silicon substrate having a first surface and a second surface opposite said first surface; B. a second single crystalline silicon substrate connected to a side of saidfirst surface of said first single crystalline silicon substrate with an insulating layer interposed therebetween; C. said first single crystalline silicon substrate being divided by a trench extending from said second surface to said first surface; i.a movable beam portion surrounded by said trench, said movable beam portion being supported by said second single crystalline silicon substrate through said insulating layer to be displaceable in a direction parallel to said first surface of said firstsingle crystalline silicon substrate, said movable beam portion having a movable electrode, ii. a stationary portion disposed to be spaced apart from said movable beam via said trench, having a stationary electrode which faces said movable beam via saidtrench to form a pair of capacitive electrodes with said movable electrode, and fixed to said second single crystalline silicon substrate; and D. an insulator covering at least one of a surface of said movable electrode and a surface of said stationaryelectrode..].

.[.21. An acceleration sensor according to claim 20, further comprising a signal-processing circuit defined in the first single crystal silicon substrate for carrying out a processing operation based on a change of a capacitance between saidmovable electrode and said stationary electrode..].

.Iadd.22. A semiconductor dynamic amount sensor comprising: a silicon layer; a silicon substrate located on the lower side of said silicon layer and electrically insulated from the silicon layer with an insulating layer provided on aperipheral portion of the silicon substrate interposed therebetween; said silicon layer including: a support beam having a mass portion which is horizontally displaceable according to a degree of dynamic amount; an insulating groove extending throughthe entire thickness of the silicon layer around the entire periphery of the support beam; and stationary portions provided spaced apart from both sides of said support beam via said insulating groove and fixed to said silicon substrate; wherein saidinsulating layer forms a gap between the upper surface of said silicon substrate and the lower surface of said support beam and mass portion..Iaddend.

.Iadd.23. The semiconductor dynamic amount sensor according to claim 22, wherein at least lateral surfaces of said support beam and said stationary portions facing said insulating groove are made of a silicon material having a lowresistivity..Iaddend.

.Iadd.24. The semiconductor dynamic amount sensor according to claim 23, wherein a highly concentrated n.sup.+ electrode is provided on said support beam and said stationary portions..Iaddend.

.Iadd.25. The semiconductor dynamic amount sensor according to claim 22, wherein said silicon layer comprises therein a signal-processing circuit for processing signal resulting from an action of said mass portion..Iaddend.

.Iadd.26. The semiconductor dynamic amount sensor according to claim 25, wherein said signal-processing circuit is a closed-loop circuit..Iaddend.

.Iadd.27. The semiconductor dynamic amount sensor according to claim 22, wherein said support beam has a thickness greater than a width thereof..Iaddend.

.Iadd.28. The semiconductor dynamic amount sensor according to claim 22, wherein said support beam has a thickness in the direction of the silicon layer thickness greater than a width in the direction of the silicon substrate surface..Iaddend.

.Iadd.29. The semiconductor dynamic amount sensor according to claim 28, wherein at least either of the surface of said support beam and the surface of said stationary portions facing said mass portion is covered with an insulatingmaterial..Iaddend.

.Iadd.30. The semiconductor dynamic amount sensor according to claim 22, wherein at least either of the surface of said support beam and the surface of said stationary portions facing said mass portion is covered with an insulatingmaterial..Iaddend.

.Iadd.31. The semiconductor dynamic amount sensor according to claim 22, wherein said silicon layer comprises a single crystal silicon and has a resistivity of 1 to 20.OMEGA.cm..Iaddend.

.Iadd.32. The semiconductor dynamic amount sensor according to claim 22, wherein said support beam is set to have an almost constant electrical potential..Iaddend.

.Iadd.33. A semiconductor dynamic amount sensor comprising: a silicon layer; a silicon substrate located on the lower side of said silicon layer and electrically insulated from the silicon layer through an insulating layer provided on aperipheral portion of the silicon substrate interposed therebetween; said silicon layer including: a support beam having a movable portion comprising a weight portion which is horizontally displaceable according to a degree of dynamic amount, a movableelectrode and a beam portion; an insulating groove extending through the entire thickness of the silicon layer around the entire periphery of the support beam; and stationary portions provided spaced apart from said movable electrode via saidinsulating groove and fixed to said silicon substrate; wherein said insulating layer ensures a gap between the upper surface of said silicon substrate and the lower surface of said movable portion comprising said weight portion, said movable electrodeand said beam portion..Iaddend.

.Iadd.34. The semiconductor dynamic amount sensor according to claim 33, wherein at least surface portions of said stationary portions and said movable portion comprise a low resistant highly concentrated regions..Iaddend.

.Iadd.35. The semiconductor dynamic amount sensor according to claim 34, wherein a highly concentrated n.sup.+ electrode is provided on said support beam and said stationary portions..Iaddend.

.Iadd.36. The semiconductor dynamic amount sensor according to claim 33, wherein said silicon layer comprises therein a signal-processing circuit for processing signal resulting from an action of said movable portion..Iaddend.

.Iadd.37. The semiconductor dynamic amount sensor according to claim 36, wherein said signal-processing circuit is a closed-loop circuit..Iaddend.

.Iadd.38. A semiconductor dynamic amount sensor comprising: a silicon layer; a silicon substrate located on the lower side of said silicon layer and electrically insulated from the silicon layer through an insulating member provided on aperipheral portion of the silicon substrate; said silicon layer including: a first movable portion comprising a weight portion which is horizontally displaced according to a degree of dynamic amount, a movable electrode and a beam portion; a secondmovable portion different from said first movable portion is provided to said silicon substrate in such a manner that said second movable portion is electrically insulated from said first movable portion via an insulating material and is movable in adirection perpendicular to the moving direction of said first movable portion; an insulating groove extending through the entire thickness of the silicon layer around the entire periphery of the support beam; and stationary portions facing and spacedapart from said movable electrode via said insulating groove and fixed to said silicon substrate; wherein said insulating member ensures a gap between the upper surface of said silicon substrate and the lower surface of said first movable portioncomprising said weight portion, said movable electrode and said beam portion..Iaddend.

.Iadd.39. The semiconductor dynamic amount sensor according to claim 38, wherein a third movable portion different from said movable portion and said second movable portion is provided to said silicon substrate in such a manner that said thirdmovable portion is electrically insulated from said movable portion and said second movable portion via an insulating material and is movable in a direction perpendicular to the moving directions of said movable portion and said second movableportion..Iaddend.

.Iadd.40. The semiconductor dynamic amount sensor according to claim 33, wherein said first movable portion is set to have an almost constant electrical potential..Iaddend.

.Iadd.41. A semiconductor dynamic amount sensor comprising: a silicon layer; a silicon substrate located on the lower side of said silicon layer and electrically insulated from the silicon layer with an insulating layer provided on aperipheral portion of the silicon substrate interposed therebetween; said silicon layer including: a support beam having a mass portion which is horizontally displaceable; stationary portions provided spaced apart from said support beam via aninsulating groove and fixed to said silicon substrate; and an insulating groove extending through the entire thickness of the silicon layer to insulate the support beam from stationery portions; wherein said insulating layer forms a gap between theupper surface of said silicon substrate and the lower surface of said support beam and said mass portion..Iaddend.

.Iadd.42. The semiconductor dynamic sensor according to claim 33, wherein the sensor is able to detect a dynamic amount in a direction X and a dynamic amount in a direction Y..Iaddend.

.Iadd.43. The semiconductor dynamic sensor according to claim 33, wherein the sensor is able to detect a dynamic amount in a direction X, a dynamic amount in a direction Y, and a dynamic amount in a direction perpendicular to the direction Xand the direction Y..Iaddend.

.Iadd.44. The semiconductor dynamic sensor according to claim 41, wherein the sensor is able to detect a dynamic amount in a direction X and a dynamic amount in a direction Y..Iaddend.

.Iadd.45. The semiconductor dynamic sensor according to claim 41, wherein the sensor is able to detect a dynamic amount in a direction X, a dynamic amount in a direction Y, and a dynamic amount in a direction perpendicular to the direction Xand the direction Y..Iaddend.
Description: BACKGROUND OF THE INVENTION

1. Field of the Invention

The present invention relates to an acceleration sensor, and more specifically, a semiconductor type acceleration sensor suitable for a air-bag system, a suspension control system, or the like, for automobiles.

2. Description of the Related Art

In producing a semiconductor type acceleration sensor, the movable part thereof has hitherto been prepared in such a way that it penetrates a single crystal silicon wafer. Accordingly, the movable part must be sized so as to penetrate throughthe thickness of a wafer, and therefore, it has been difficult to miniaturize the acceleration sensor. In addition, in order to incorporate this sensor into a package, a relaxation part, have been required such as a pedestal, in order to release thestress caused by the difference in coefficients of thermal expansion or the like.

However, in Nikkei Electronics, Nov. 11, 1991 (No. 540), pp 223 to 231, there is illustrated an acceleration sensor produced by use of a surface micro-machining technique. According to this technique, a thin polysilicon film is laminated on asilicon substrate, and this polysilicon film is etched, whereby a beam movable parallel to the surface of the substrate is formed, so as to form a differential capacity type acceleration sensor. However, when a beam structure is formed by use ofpolysilicon, if a signal processing circuit is formed around the formed beam structure, the sensor characteristics become unstable. This is because the beam structure is formed of a polycrystalline and amorphous material, resulting in noticeablevariation for every production lot. Accordingly, it is still desirable to form an acceleration sensor by surface micro-machining single crystal silicon.

Under such circumstances, the purpose of the present invention is to provide an acceleration sensor having a novel structure, by which high precision and high reliability can be realized.

In addition, another purpose of the present invention is to produce this acceleration sensor with a good yield rate during the production process thereof.

SUMMARY OF THE INVENTION

The gist of a first embodiment of the present invention resides in an acceleration sensor, comprising a second single crystal silicon substrate bonded onto a first single crystal silicon substrate with an insulating film interposed therebetween,the second single crystal silicon substrate being made of a thin film, a beam formed on at least either of said first and second single crystal silicon substrates and movable in a direction parallel to the surface thereof, and a signal-processing circuitformed on at least one of said first and second single crystal silicon substrates for performing processing of signals produced by a movement of beam, caused by an acceleration.

In addition, the gist of a second embodiment of the present invention resides in a process for producing an acceleration sensor, comprising; a first step of forming, on a main surface of a first single crystal silicon substrate, a groove with apredetermined depth for formation of a beam; a second step of forming, on the main surface of said first single crystal silicon substrate, a film of a polycrystalline silicon, an amorphous silicon or a mixture thereof so as to fill said groove with saidsilicon film, and smoothing (flattening) the surface of said silicon film; a third step of bonding the main surface of said first single crystal silicon substrate to a second single crystal silicon substrate with an insulating film formed thereon, saidinsulating film being interposed between said first and second single crystal silicon substrates; a fourth step of polishing the reverse side of said first single crystal silicon substrate to a predetermined degree, so as to make said first singlecrystal silicon substrate a thin film; and a fifth step of forming a signal-processing circuit on at least either of said first and second single crystal silicon substrates, and thereafter, removing by etching said silicon film of a polycrystal silicon,an amorphous silicon or a mixture thereof from said reverse side of said first single crystal silicon substrates, to form a beam.

In addition, the gist of a third embodiment of the present invention resides in a process for producing an acceleration sensor, comprising; a first step of bonding a main surface of a first single crystal silicon substrate to a second singlecrystal silicon substrate with an insulating film formed thereon, said insulating film being interposed therebetween; a second step of polishing the reverse side of said first single crystal silicon substrate to a predetermined degree, so as to make thefirst single crystal silicon substrate a thin film; a third step of forming a groove with a predetermined depth for formation of a beam; a fourth step of forming, on the reverse side of said first single crystal silicon substrate, a film of a polycrystalsilicon, an amorphous silicon or a mixture thereof, so as to fill said groove with said silicon film, and smoothing the surface of said silicon film; and a fifth step of forming a signal-processing circuit on at least one of said first and second singlecrystal silicon substrates, and thereafter, removing by etching said film of polycrystal silicon, amorphous silicon or a mixture thereof from the reverse side of the first single crystal silicon substrate, to form a beam.

In the first embodiment, when an acceleration is applied in a direction parallel to the surface of the bonded single crystal silicon substrates, the beam formed on the first or second single crystal silicon substrate moves. As this beam moves,signal processing is performed in the signal-processing circuit formed on the first or second single crystal silicon substrate.

In the second embodiment, as a first step, a groove of a predetermined depth for formation of a beam is formed on the main surface of the first single crystal silicon substrate, and as a second step, a film of a polycrystalline silicon, anamorphous silicon or a mixture thereof is formed on the main surface of the first single crystal silicon substrate, whereby the groove is filled with the silicon film, and the surface of this silicon film is flattened. Subsequently, as a third step, themain surface of the first single crystal silicon substrate is bonded to a second single crystal silicon substrate having an insulating film formed thereon, said insulating film being interposed between the first and second single crystal substrates, and,as a fourth step, the reverse side of the first single crystal silicon substrate is polished to a predetermined degree, whereby the first single crystal silicon substrate is made into a thin film. Subsequently, as a fifth step, a signal-processingcircuit is formed on the first or second single crystal silicon substrate, thereafter the polycrystalline, amorphous or mixed silicon film is removed by etching from the reverse side of the first single crystal silicon substrate, and a beam is formed. As a result, an acceleration sensor according to the first invention is produced.

In the third embodiment, as a first step, the main surface of a first single crystal silicon substrate is bonded to a second single crystal silicon substrate with an insulating film formed thereon, said insulating film being interposed betweenthe first and second substrates, and as a second step, the reverse side of the first single crystal silicon substrate is polished to a predetermined degree, so that the first single crystal silicon substrate is made into a thin film. Subsequently, as athird step, a groove of a predetermined depth for formation of a beam is formed on the reverse side of the first single crystal silicon substrate, and as a fourth step, a film of polycrystalline silicon, an amorphous silicon or a mixture thereof isformed on the reverse side of the first single crystal silicon substrate, whereupon the groove is filled with the silicon film, and the surface of the silicon film is flattened. Subsequently, as a fifth step, a signal-processing circuit is formed on thefirst or second single crystal silicon substrate, whereafter the polycrystalline, amorphous or mixed silicon film is removed by etching from the reverse side of the first single crystal silicon substrate, and a beam is formed. As a result, anacceleration sensor according to the first embodiment is produced.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a plan of an acceleration sensor according to the first embodiment of the present invention;

FIG. 2 is a cross section taken along line 2--2 in FIG. 1;

FIGS. 3 to 10 are illustrations for explanation of the manufacturing process of the first embodiment, and, respectively, a sectional view for each production stage;

FIG. 11 is a plan illustrating an application example of the first embodiment;

FIG. 12 is a sectional view taken along the line 12--12 in FIG. 11;

FIGS. 13 to 21 are illustrations for explanation of the manufacturing process of the second embodiment, and, respectively, a sectional view for each production stage;

FIGS. 22 to 28 are illustrations for explanation of the manufacturing process of the third embodiment, and, respectively, a sectional view for each production stage;

FIGS. 29 to 31 are illustrations for explanation of the manufacturing process of the fourth embodiment, and, respectively, a sectional view for each production stage;

FIGS. 32 to 34 are illustrations for explanation of the manufacturing process examples to which the fourth embodiment is applied, and, respectively, a sectional view for each production stage;

FIG. 35 is a plan illustrating an example of a sensor tip formed by an acceleration sensor according to the present invention.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS OF THE INVENTION

In the following, the embodiments and realizations of the present invention, will be explained with reference to the attached drawings.

First Embodiment

FIG. 1 is a plain view plan of an acceleration sensor produced by the first embodiment of the present invention, and FIG. 2 is a sectional view taken along line 2--2 in FIG. 1. In addition, in the present embodiment, the sensor part and thesignal-processing circuit are formed of the same single crystal silicon substrate.

The present acceleration sensor is a capacity type acceleration sensor. As illustrated in FIG. 2, there is bonded onto a single crystal silicon substrate 8 a single crystal silicon substrate 1 through an SiO.sub.2 film 9, and in the singlecrystal silicon substrate 1, there is formed a cantilever 13 by a trench 3 penetrating said substrate 1. As illustrated in FIG. 1, this cantilever 13 has a structure such that an end side thereof is branched into two parts. The cantilever 13 can bemoved in a direction parallel to the surface of the single crystal silicon substrate 1 (the arrow direction C in FIG. 1). In addition, in the single crystal silicon substrate 1, a signal-processing circuit 10 is formed and is electrically insulated fromthe cantilever 13 by a polysilicon film 6 and an SiO.sub.2 film 5.

In the following, the production precess of the first embodiment of the present invention, which is suitable for the production of the aforesaid structure, will be explained with reference to FIGS. 3 to 10.

First, as illustrated in FIG. 3, an n-type (100) single crystal silicon substrate 1 with a resistance of 1 to 20.OMEGA.cm is provided, and on the main surface thereof, there is formed an SiO.sub.2 film 2 with a thickness of about 1 .mu.m bythermal oxidation, and the SiO.sub.2 film 2 is formed into a predetermined pattern by a photolithographic method. This pattern is a pattern exposing, on the main surface of the silicon substrate, an area to be formed as a groove separating at least anarea to be formed as a movable electrode (cantilever) from the substrate, and in the present embodiment, this pattern is formed as a pattern exposing also the main surface of the silicon substrate in an area for transversely insulating and separating thesignal-processing circuit. Subsequently, on the main surface side of the single crystal silicon substrate 1, there is formed a trench 3 having a perpendicular wall with a predetermined depth, e.g. ranging from about 0.2 to about 30 .mu.m. In thepresent embodiment, explanation will be made with respect to the case where the wall thickness is about 3 .mu.m.

Subsequently, after the SiO.sub.2 film 2 has been removed, as illustrated in FIG. 4, an n.sup.+ diffused layer 4 formed using phosphorus, arsenic or the like is formed on the main surface of the single crystal silicon substrate 1, including theinternal wall of the trench 3, and further, an SiO.sub.2 film 5 with a thickness ranging from 0.1 to 1 .mu.m is formed by thermal oxidation or the like. In this case, in order to prevent damage by etching, there may be conducted the so-called "sacrificeoxidation" in which SiO.sub.2 is formed by thermal oxidation and removed before formation of the n.sup.+ diffused layer 4.

Subsequently, as illustrated in FIG. 5, a polysilicon film 6 is formed on the main surface of the single crystal silicon substrate 1, and the trench 3 is filled with the polysilicon film 6. In addition, in the case where an impurity isintroduced into the polysilicon film 6 in order to use the polysilicon film 6 as a conductive path, forming a thin polysilicon layer and diffusing phosphorus or the like in a high concentration before formation of the polysilicon film 6, allows theimpurity to be introduced into the polysilicon film 6.

Next, as illustrated in FIG. 6, the surface of the polysilicon film 6 is mirror finished, so as to make the thickness of the polysilicon film 6 a predetermined value. Subsequently, boron ions or other impurity are implanted into the polysiliconfilm 6 to form p.sup.+ diffused layers 7 in predetermined areas.

On the other hand, as illustrated in FIG. 7, another (100) single crystal silicon substrate 8 is provided, and an SiO.sub.2 film 9 with a thickness ranging from 0.1 to 1.0 .mu.m is formed on the main surface of the silicon substrate 8.

Subsequently, the single crystal silicon substrate 1 and the single crystal silicon substrate 8 are dipped into e.g. an aqueous mixed solution of aqueous hydrogen peroxide and sulfuric acid, so as to subject these substrates to ahydrophilicity-imparting treatment. Thereafter, these substrates are dried, and as illustrated in FIG. 8, the main surface of the single crystal silicon substrate 1 and that of the single crystal silicon substrate 8 are put together at room temperature,and these substrates are introduced into a furnace at 400 to 1100.degree. C. for a period of time ranging from 0.5 to 2 hours, so as to strongly bond them.

Subsequently, as illustrated in FIG. 9, by use of an aqueous solution of an alkali type, e.g. an aqueous KOH solution or the like, the reverse side of the single crystal silicon substrate 1 is subjected to selective polishing. The polishing iscontinued until the SiO.sub.2 film 5 is exposed. As a result, the thickness of the single crystal silicon substrate 1 reaches a value which is approximately determined by the depth of the trench, e.g. about 3 .mu.m, so that the substrate 1 is made thin.

Subsequently, as illustrated in FIG. 10, in a predetermined area of the single crystal silicon substrate 1, there is formed a single-processing circuit 10 (IC circuit portion) by use of an ordinary CMOS process, bipolar process or the like. Inaddition, a diffused layer for connecting to wiring and a metallic electrode film composed of an aluminum film or the like are formed, and wiring at the sensor part, wiring at the circuit part, and connection of the sensor part of the circuit part areperformed. In FIG. 1 and FIG. 10, a MOS transistor alone is illustrated as a part of the signal-processing circuit 10.

Further, on the upper surface of the signal-processing circuit 10, there is formed, as a passivation film 11, a plasma SiN film (P-SiN) e.g. by a plasma CD method. Subsequently, at the sensor part side, windows 12 are opened at predeterminedareas of the passivation film 11, and the polysilicon film 6 filled in the trench 3 is exposed from the surface. By this window opening procedure, the single crystal portions where a cantilever or fixed electrodes are to be formed are demarcated fromthe polycrystal portions embedded in the trench, on the surface of the substrate.

Subsequently, as illustrated in FIG. 2, by use of a 20% solution of TMAH (tetramethylammonium hydroxide) (CH.sub.3).sub.4NOH, the polysilicon film 6 is removed by etching through the windows 12 of the passivation film 11, from the reverse side(the upper side in FIG. 2) of the single crystalline silicon substrate 1. In this case, the passivation film 11 (P-SiN), SiO.sub.2 film 5, aluminum wiring layer and p.sup.+ diffused layer (p.sup.+ polysilicon film) 7 are hardly etched by the selectiveetching. Accordingly, the bonding of the single crystal silicon substrate to the lower single crystal silicon substrate 8 is secured through the p.sup.+ diffused layer (p.sup.+ polysilicon film) 7.

In addition, if trenches 3 are preliminarily formed also in the wide area of the cantilever 13 in FIG. 1, and etching windows 48 are provided simultaneously with the formation of the windows 12, in such a way that the etching windows 48communicate with said trenches 3, the polysilicon film 6 below the movable part (cantilever 13) of the sensor can be more securely removed by etching through this etching window 48 when the polysilicon film 6 is removed by etching.

By the aforesaid procedures, the cantilever 13 is formed. In this case, the cantilever 13 becomes, as illustrated in FIG. 2, smaller in the thickness L2 in a direction parallel to the surface of the single crystal silicon substrate 1 than in thethickness L1 in a direction along the depth of the single crystal silicon substrate 1.

In a capacity type acceleration sensor, the end portions (bifurcated portions) of the cantilever 13 are formed as movable electrodes, and as illustrated in FIG. 1, the parts of the single crystal silicon substrate 1, opposing the end portions ofthe cantilever 13, are formed as fixed electrodes 14, 15, 16, and 17, respectively. In addition, as illustrated in FIG. 1, fixed electrode 14 and fixed electrode 16 are derived through an aluminium wiring layer 18a, fixed electrode 15 and fixedelectrode 17 are derived through an aluminium wiring layer 18b, and the cantilever 13 (movable electrode) is derived through an aluminium wiring layer 18c. These aluminium wiring layers 18a, 18b, and 18c are connected to the signal-processing circuit10, and by this signal-processing circuit 10, signal processing is conducted as the cantilever (movable electrode) 13 is displaced owing to an acceleration. In addition, by the n.sup.+ diffused layers 4 (see FIG. 2) disposed on the cantilevers 13(movable electrodes) and fixed electrodes 14, 15, 16, and 17, the electric potential is maintained at a constant value.

Although a capacity type acceleration sensor is made in the present embodiment, if a piezo resistance layer is formed at the surface of the root portion of the cantilever 13, a piezo resistance type acceleration sensor can be formed. As a matterof course, if these two types of sensors are formed in a one and same substrate, the precision and reliability of the acceleration sensor can further be improved.

In the acceleration sensor thus produced, the single crystal silicon substrate 1 is bonded through an SiO.sub.2 film to the single crystal silicon substrate 8, so as to form an SOI structure. In addition, in the cantilever 13, its thickness L2in a direction parallel to the surface of the single crystal silicon substrate 1 is smaller than the thickness L1 in a direction of the depth of the single crystal silicon substrate 1. Accordingly, the cantilever 13 becomes movable, on the surface ofthe single crystal silicon substrate 1, in a direction parallel to the surface, whereby an acceleration to a direction parallel to the substrate surface is detected.

As mentioned in the foregoing, in the present embodiment, on the main surface of the single crystal silicon surface 1, there is formed a trench (groove) 3 of a predetermined depth for formation of the cantilever 13 (the first step), and thepolysilicon film 6 is formed on the main surface of the single crystal silicon substrate 1, so as to fill the trench 3 with said polysilicon film 6, and the surface of the polysilicon film 6 is flattened (smoothed) (the second step). Subsequently, themain surface of the single crystal silicon substrate 1 is bonded to the single crystal silicon substrate 8 with an SiO.sub.2 film 9 (insulating film) formed thereon, through said SiO.sub.2 film 9 being interposed between the substrates 1 and 8 (the thirdstep), whereafter the reverse side of the single crystal silicon substrate 1 is polished to a predetermined degree, so as to make the single crystalline silicon substrate into a thin film (the fourth step). Subsequently, the signal-processing circuit 10is formed on the surface of the single crystal silicon substrate, whereafter the polysilicon film 6 is removed by etching from the reverse side of the single crystal silicon substrate, so as to form the cantilever 13 (the fifth step).

Accordingly, during the process for the formation of the signal-processing circuit 10, in the course of the wafer process, the trench 3 in the surface portion of the single crystal silicon substrate, is filled with the polysilicon film 6, wherebycontamination of the IC elements, contamination of production equipment, and degradation or deterioration of electrical properties accompanied therewith can be prevented. That is, in the wafer process, by contriving to prevent the surface structuressuch as concave portions or penetration holes from appearing on the wafer surface in the heat treatment, photolithographic treatment and the like, in the course of the process, it is possible to prevent contamination and the like, and to thereby stablyprovide acceleration sensors of high precision.

The thus produced acceleration sensor comprises the single crystal silicon substrate 1, which is bonded through an SiO.sub.2 film (insulating film) to the single crystal silicon substrate 8, and which is made a thin film; the cantilever 13, whichis formed on said single crystal silicon substrate 1 and which is movable in a direction parallel to the surface of the substrate; and the signal-processing circuit 10, which is also formed on the single crystal silicon substrate 1 and which performssignal processing as the cantilever 13 moves owing to an acceleration. When an acceleration is applied in a direction parallel to the surface of the single crystal silicon substrate 1, the cantilever formed on the single crystal silicon substrate 1moves. As the cantilever 13 moves, signal-processing is performed by the signal-processing circuit 10 formed on the single crystal silicon substrate 1. In such a way as above, by a micro-machining technique using single crystal silicon, an accelerationsensor is formed, by the novel structure of which high precision and high reliability can be realized.

In addition, since the surface of the aforesaid cantilever 13 and the part of the single crystal silicon substrate 1, opposing said cantilever 13, are coated with the SiO.sub.2 film (insulator) 5, electrode short-circuit in the capacity typeacceleration sensor can previously be prevented. In addition, it suffices if at least either of the surface of the cantilever 13 or the part of the single crystal silicon substrate 1 opposing the cantilever 13 is coated with the SiO.sub.2 film(insulator) 5.

Further, as an application of the present embodiment, as illustrated in FIGS. 11 and 12, the cantilever may be separated from the signal-processing circuit (IC circuit portion) 10 and an air bridge wiring is formed, in order to reduce parasiticcapacity. In addition, the fixed electrodes 14, 15, 16, and 17 may be formed so as to have the same structure as above. This can be realized by forming a p.sup.+ type polysilicon film 7 at the minimum position necessary for bonding the fixed electrodesto the lower substrate.

In addition, although an aluminium wiring layer is used in the aforesaid embodiment, the wiring part may be formed by use of a polysilicon layer. Further, although two movable electrodes are formed at the end of the beam and simultaneously, fourfixed electrodes 14, 15, 16, and 17 are formed, in the aforesaid embodiment, the movable and fixed electrodes may be formed like the teeth of a comb in order to further improve the sensitivity of the sensor.

In addition, an oxide film may selectively be formed, instead of the formation of the p.sup.+ polysilicon film 7.

Second Embodiment

Next, there will be made explanations about the production process of the second embodiment, emphasizing the points that are different from those in the first embodiment. In addition, in the second embodiment to be hereafter explained,explanations will be made by way of an example of a case where a sensor having a structure according to the structure illustrated in FIGS. 1 and 2, as explained in the aforesaid first embodiment, and there will be illustrated a sectional viewcorresponding to the 2--2 section of FIG. 1.

In the aforesaid first embodiment, in order to form the cantilever 13, the p.sup.+ diffused layer (p.sup.+ polysilicon film) 7 is formed for the purpose of separating the cantilever portion from the single crystal silicon substrate at apredetermined distance, but in second present embodiment, a concave portion is formed before formation of a trench, for the purpose of separating the cantilever from the substrate at a predetermined distance.

In FIGS. 13 to 21, the production process is illustrated.

First, as illustrated in FIG. 13, an n type (100) single crystal silicon substrate 20 is provided, and on the main surface of the provided single crystal silicon substrate 20, there is formed a concave portion 21 with a predetermined depth e.g.ranging from 0.1 to 5 .mu.m. Subsequently, as illustrated in FIG. 14, on the main surface of the single crystal silicon substrate 20, there is formed an SiO.sub.2 film 22, and a pattern is formed by a photolithographic means, in the same way as in theaforesaid first embodiment. Subsequently, on the main surface of the single crystal silicon substrate 20 including the bottom of the concave portion 21, there is formed a trench with a depth ranging from about 0.1 to about 30 .mu.m (3 .mu.m in thepresent embodiment) by dry etching or the like.

Subsequently, as illustrated in FIG. 15, on the main surface of the single crystal silicon substrate 20 including the internal wall of the trench 23, there is formed an n.sup.+ diffused layer 24, and an SiO.sub.2 film 25 is formed by thermaloxidation. Thereafter, as illustrated in FIG. 16, a polysilicon film 26 is deposited in the trench 23 by the LPCVD method.

Subsequently, as illustrated in FIG. 17, the surface of the polysilicon film 26 is polished by use of the SiO.sub.2 film as an etching stopper, so as to smooth the surface. In the above case, although it is desirable that the surface of thepolysilicon film 26 and the SiO.sub.2 film 25 become smooth, even if the polysilicon film 26 is rather indented, so long as the surface of the SiO.sub.2 film is made smooth, no inconvenience is caused in the subsequent wafer cementing.

On the other hand, as illustrated in FIG. 18, another (100) single crystal silicon substrate 27 is provided, and, on the main surface of the substrate 27, there is formed an SiO.sub.2 film with a thickness ranging from 0.1 to 1.0 .mu.m by thermaloxidation of the substrate. Subsequently, single crystal silicon substrates 20 and 27 are dipped in e.g. a solution of an aqueous hydrogen per oxide and sulfuric acid, so as to subject them to a hydrophilicity-imparting treatment. Subsequently, thesubstrates are dried, and thereafter, the main surfaces of the two single crystal silicon substrates 20 and 27 are put together at room temperature, and introduced into a furnace at 400 to 1100.degree. C. for a period of time ranging from 0.5 and 2hours, so as to strongly bond the two surfaces.

Subsequently, as illustrated in FIG. 19, the reverse side of the single crystal silicon substrate 20 is subjected to selective polishing by use of an aqueous solution of alkali type, e.g. an aqueous KOH solution. The selective polishing isperformed until the SiO.sub.2 film 25 appears on the surface. As a result, the thickness of the single crystal silicon substrate 20 becomes e.g. about 3 .mu.m, so as to be made a thin film.

Subsequently, as illustrated in FIG. 20, a signal-processing circuit (IC circuit portion) 10 is formed through an ordinary CMOS process, bipolar process, or the like. Further, on the upper surface of the signal-processing circuit 10, there isformed, as a passivation film 11, a plasma SiN film (P-SiN film) by e.g. plasma CVD method. Subsequently, windows 12 are opened at predetermined areas of the passivation film 11, and the polysilicon film 20 is exposed to the surface at the sensorportion.

Subsequently, as illustrated in FIG. 21, by use of a 20% solution of TMAH (tetramethylammonium hydroxide) (CH.sub.3).sub.4NOH, the polysilicon film 26 is removed by etching from the reverse side of the single crystal silicon substrate 20 throughthe windows 12 on the passivation film 11. In the above case, the passivation film 11 (P-SiN), SiO.sub.2 film, and aluminium wiring layer are hardly etched by the selective etching.

As a result, a cantilever 13 is formed.

Also by the present embodiment, there is obtained the same effect as in the aforesaid first embodiment.

Third Embodiment

Next, there will be made explanations about the production process in the third embodiment, laying stress on the differential points between the first and third embodiments.

Although, in the aforesaid first and second embodiments, the trench is filled with polysilicon before the bonding of the wafers, in the present embodiment, the trench is filled with polysilicon after the bonding of wafers, and in the final stage,the thus filled polysilicon is removed, so as to produce an acceleration sensor.

In FIGS. 22 to 28, the production process is illustrated.

First, as illustrated in FIG. 22, an n-type (100) single crystal silicon substrate 30 is provided, and on the main surface of the provided single crystal silicon substrate 30, there is formed a concave portion 31 in a depth ranging from 0.1 to 5.mu.m, in the same way as in the aforesaid second embodiment. On the other hand, as illustrated in FIG. 23, a single crystal silicon substrate 32 is provided, and an SiO.sub.2 film is formed by thermal oxidation on the main surface of the single crystalsilicon substrate 31. Thereafter, the main surface of the single crystal silicon substrate 30 is bonded to the main surface of a single crystal silicon substrate 32.

Subsequently, as illustrated in FIG. 24, the reverse side of the single crystal silicon substrate 30 is subjected to mirror polishing to a predetermined thickness (0.1 to 30 .mu.m). Thereafter, as illustrated in FIG. 25, there is formed anSiO.sub.2 film 34 to a thickness ranging from 0.1 to 2 .mu.m, following which the SiO.sub.2 film is subjected to patterning, and a trench 35 is formed by etching. Thereby, a cantilever 13 and a transversal insulatedly separated area of the processingcircuit portion are formed.

Next, by thermal diffusion or the like, there is introduced an N type impurity of arsenic or phosphorus in a high concentration, and a highly concentrated n.sup.+ layer 36 is formed in the silicon area which is not covered with SiO.sub.2 films 33and 34.

Subsequently, as illustrated in FIG. 26, a thermal oxidation film is formed on the side wall of the trench 35 and the like, whereafter a polysilicon film 37 is formed on the surface of the single crystal silicon substrate 30, and the trench 35 isfilled with the polysilicon film 37. Thereafter, as illustrated in FIG. 27, the surface of the polysilicon film 37 is selectively polished and smoothed until the SiO.sub.2 film 34 appears on the surface. Further, as illustrated in FIG. 28, asignal-processing circuit 10 is formed, and finally, the polysilicon film 37 is removed by etching from the reverse side (upper surface side) of the single crystal silicon substrate 30, so as to again separate the cantilever 13 from the substrate toallow it to move.

As described above, in the present third embodiment, the main surface of the single crystal silicon substrate 30 is bonded to the single crystal silicon substrate 32 with the SiO.sub.2 film (insulating film) 33 formed thereon, through saidSiO.sub.2 film 33 being interposed between the substrates 30 and 32 (first step), and the reverse side of the single crystal silicon substrate is polished to a predetermined degree, so as to make the single crystal silicon substrate 30 a thin film(second step). Subsequently, on the reverse side of the single crystal silicon substrate 30, there is formed a trench (groove) 35 with a predetermined depth for formation of a cantilever 13 (third step), and the trench 35 is filled with the polysiliconfilm 37, and the surface of the polysilicon film 37 is smoothed (fourth step). Subsequently, a signal-processing circuit is formed on the single crystal silicon substrate 30, whereafter the polysilicon film 37 is removed, by etching, from the reverseside of the single crystal silicon substrate 30, so as to form a cantilever 13 (fifth step).

Therefore, in the process of formation of the signal-processing circuit 10 in the wafer, the trench 35 is filled with the polysilicon film 37 in the upper surface part of the single crystal silicon substrate 30, whereby contamination of the ICelements, contamination of the production apparatus, and degradation or deterioration of electrical properties attended therewith can be prevented. That is, by contriving not to make a surface structure such as a concave portion or a perforation of thelike appear on the wafer surface in the heat treatment, the photolithographical treatment or the like in the course of the wafer process, contamination and the like can be prevented, so as to stabilize the wafer process, and a stable supply ofacceleration sensors, of high precision, can be produced.

Fourth Embodiment

In the following, there will be made explanations about the production process of the fourth embodiment, laying stress on the differences between the present embodiment and the third embodiment.

The present embodiment is intended to produce an acceleration sensor at a lower cost than the production process of the third embodiment.

In FIGS. 29 to 31, the production process is illustrated.

First, as illustrated in FIG. 29, an SiO.sub.2 film with a thickness ranging from 0.1 to 2 .mu.m is formed on the main surface of a single crystal silicon substrate 40, and a single crystal silicon substrate 42 is bonded to the substrate 40 so asto interpose the SiO.sub.2 film 41 between the substrates 40 and 42. Subsequently, as illustrated in FIG. 30, the upper surface of the single crystal silicon substrate 42 is polished so as to make the thickness of the single crystal silicon substrate apredetermined value. That is, the thickness of the single crystal silicon substrate 42 is reduced to e.g. about 3 .mu.m. Thereafter, a highly concentrated n.sup.+ diffused layer 43 is formed on the upper surface of the single crystal silicon substrate42, and further, an SiO.sub.2 film 44 is formed thereon. It suffices if this highly concentrated n.sup.+ diffused layer 43 is formed corresponding to the parts of the sensor which will be formed as movable electrodes and fixed electrodes.

Subsequently, as illustrated in FIG. 31, patterning is applied to an SiO.sub.2 film, as in the third embodiment, and a trench 45 is formed on the single crystal silicon substrate 42. Thereafter, the SiO2 film 41 below this trench 45 is partlyremoved by etching with an aqueous hydrofluoric acid solution. In this case, a part of SiO.sub.2 film 41, below the part to be formed as a cantilever 13, is completely removed, and another part of the SiO.sub.2 film 41, below the part to be formed assolid electrodes and signal-processing circuit portion, is left. Because the lower portion of the part is to be formed as the cantilever 13 it is narrower than with the other part. In addition, in the above case, the highly concentrated n.sup.+diffused layer 43 is separated into the cantilever 13 and fixed electrodes.

Subsequently, through the same processes as illustrated in FIGS. 26 to 28, there is produced a capacity type acceleration sensor.

In the following, there will be explained application examples of the fourth embodiment with reference to FIGS. 32 to 34.

First, as illustrated in FIG. 32, an SiO.sub.2 film with a thickness ranging from 0.1 to 2 .mu.m is formed on the main surface of the single crystal silicon substrate 40, and a concave portion 47 with a depth ranging from 0.1 to 3 .mu.m is formedat the area of the main surface of the single crystal silicon substrate 42, on which area a cantilever is to be formed. Subsequently, the main surface of the single crystal silicon substrate 42 is bonded to the main surface of the single crystal siliconsubstrate 40, the SiO.sub.2 film 41 being put therebetween. Further, as illustrated in FIG. 33, the upper surface of the single crystal silicon substrate 42 is polished so as to give the single crystal silicon substrate 42 a predetermined thickness. That is, the thickness of the single crystal silicon substrate 42 is made thin to a value of about 3 .mu.m. Subsequently, the aforesaid highly concentrated diffused layer 43 is formed on the upper surface of the single crystal silicon substrate 42, andan SiO.sub.2 film 44 is formed thereon.

Subsequently, as illustrated in FIG. 34, onto the single crystal silicon substrate 42, there are formed trenches 45 extending to the concave portions 47, and cantilevers 13 are formed.

Thereafter, a capacity type acceleration sensor is produced through the same processes as illustrated in FIGS. 26 to 28.

By conducting the aforesaid procedures, electrical insulation can be made more securely as compared with the case where the SiO.sub.2 film 41 is partly removed by etching. In addition, the mechanical strength of the sensor can be improved.

In addition, the present invention is not restricted to the aforesaid embodiments, and is applicable to a twin-lever spring or a polyever spring embodiment, in addition to a cantilever spring embodiment.

In addition, as illustrated in FIG. 35, it is possible to form two acceleration sensors 13a and 13b onto a single crystal silicon substrate 50, for detecting the acceleration in the direction X by the acceleration sensor 13a, and the accelerationin the direction Y by the acceleration sensor 13b. Further, it is possible to form an acceleration sensor capable of detecting the acceleration in a direction surface perpendicular to these X and Y direction acceleration sensors 13a and 13b, on the samesubstrate, so as to detect an acceleration in three-dimensionals. In addition, when the present acceleration sensor is used as a capacity type acceleration sensor, it is possible to further stabilize the properties by forming the present accelerationsensor into a so-called "servo type" sensor (with a closed-loop circuit).

In addition, in the aforesaid embodiments, the trenches (grooves) 3, 23, and 35 are filled with polysilicon films 6, 26, and 37, respectively, but there may be used a film of polysilicon, amorphous silicon or a mixed silicon containingpolysilicon and amorphous silicon.

In addition, in the aforesaid embodiments, a sensor portion and a signal-processing portion are formed in the single crystal silicon substrate to be formed as the upper side, but the present acceleration sensor is not restricted to such astructure, and it is possible to utilize also a single crystal silicon substrate formed as a base, and form a sensor portion and a signal-processing portion on the lower substrate.

As described in detail in the foregoing, according to the present invention, high precision and high reliability can be realized by formatting a novel structure. In addition, when a signal-processing circuit is provided on the same chip as amovable beam, since there is produced neither a hollow part nor a groove during the production process, it is possible to make the processing stable. In addition, it is at the final step that the movable beam is made movable with respect to thesubstrate, whereby, in the case of the movable beam being bonded to the lower substrate to be formed as a pedestal or in the case of a circuit being formed, or the like, minute beams can be prevented from being broken, and the yield thereof can be madehigher. In addition, since it is a micro-machining technique which determines the shape of the present acceleration sensor, the present acceleration sensor can be produced with high precision.

[Industrial Availability]

As described in the foregoing, the present invention is useful for the production of a semi-conductor acceleration sensor having minute movable parts, and the present acceleration sensor is suitable as an acceleration sensor to be used for airbag system, suspension control system and the like of automobiles. In addition, the present invention can be applied to a capacity type acceleration sensor for detecting acceleration in multiple directions.

* * * * *
 
 
  Recently Added Patents
Advertising system and method
Distortion compensation device, distortion compensation method, and radio transmitter
Case for electronic device
Liquid crystal display device
Storage apparatus and storage apparatus management method performing data I/O processing using a plurality of microprocessors
Proximity sensor arrangement in a mobile device
Method and composition for attracting arthropods by volatizing an acid
  Randomly Featured Patents
Transporter genes OATP-B,C,D, and E
Method and system for outputting program change effect information to a user
Joint space-time optimum filters (JSTOF) for interference cancellation
Extended range power detector
Coating/developing apparatus and substrate transfer method
Process and compositions for lithographic printing in multiple layers
System and method for adaptively collecting performance and event information
Rotating head and piston engine
Ultrasound transducer
Boron resins of high selective absorbent power