Inflatable-deflatable flexible structural component |
| RE31898 |
Inflatable-deflatable flexible structural component
|
|
| Patent Drawings: | |
| Inventor: |
Suter |
| Date Issued: |
May 28, 1985 |
| Application: |
06/611,460 |
| Filed: |
May 17, 1984 |
| Inventors: |
Suter; Charles A. (Stow, OH)
|
| Assignee: |
Goodyear Aerospace Corporation (Akron, OH) |
| Primary Examiner: |
Van Balen; William J. |
| Assistant Examiner: |
|
| Attorney Or Agent: |
Milliken; P. E.Wolfe; J. D.Germain; L. A. |
| U.S. Class: |
206/522; 264/321; 264/54; 428/12; 428/178; 428/311.51; 428/317.1; 428/318.4; 428/71; 441/41; 5/709; 52/2.18; 52/22; 52/309.11; 52/309.6 |
| Field Of Search: |
5/449; 5/481; 52/2; 52/309.6; 52/309.11; 114/345; 206/522; 264/54; 264/321; 428/12; 428/71; 428/76; 428/178; 428/304.4; 428/311.1; 428/311.5; 428/317.1; 428/317.3; 428/317.5; 428/317.7; 428/318.4; 428/319.7; 441/38; 441/40; 441/41; 441/114; 441/115; 441/116 |
| International Class: |
|
| U.S Patent Documents: |
2647399; 2997100; 3028279; 3246443; 3307318; 3325338; 3378864; 3400196; 3554135; 3558417; 3667625 |
| Foreign Patent Documents: |
428124; 984604 |
| Other References: |
|
|
| Abstract: |
An inflatable-deflatable flexible structural component comprising a flexible foam core portion having a fabric covering, the fabric being sealed against loss of air by a flexible elastomeric coating. |
| Claim: |
What is claimed is:
1. An inflatable-deflatable flexible structural component comprising a flexible open celled foam core portion having a fabric covering adhered to and enclosing said foam andhaving a valve means in communication therewith, the fabric being sealed against loss of air by a flexible elastomeric coating.
2. The structural component of claim 1 wherein the foam is reticulated.
3. The structural component of claim 1 wherein the foam core is a polyurethane foam and the fabric covering the foam is nylon having a coat of polyurethane thereon. |
| Description: |
This inventionrelates to an inflatable-deflatable flexible structural component having relative dimensional stability and which can be collapsed into a package of relatively small size and to the method of manufacturing such a component.
The described structural component would be used to make inflatable-deflatable shelters, boats, shipping containers, and other articles.
Flexible inflatable-deflatable shelters, boats and shipping containers have been manufactured from rubberized fabric for many years. A major limitation in the design of such objects is that an inflatable flexible component will tend to assume around shape when inflated. Thus, inflated articles are made as a series of tubes, spheres, or other bodies with surface of revolution. This is undesirable, since it limits configuration and design flexibility and leads to a large number of separateinflated components to make an object of the desired configuration and also increases the material and construction costs.
It is an object of this invention to provide a method of making an inflatable-deflatable structural component, the walls of which will assume a shape upon inflation other than that of a surface of revolution.
The objects and advantages ofthis invention may be more readily understood and appreciated by reference to the accompanying drawing where
FIG. 1 is a perspective view of a block of foam of the shape desired and
FIG. 2 is a perspective view of the finished inflatable-deflatable structural component having portion in section to illustrate the construction features.
The above objects of this invention can be accomplished by covering an open cellfoam preferably of the reticulated type with a rubberized fabric to give a container which encloses the foam and which can be inflated by the introduction of air usually at about 5-20 pounds per square inch pressure and can be deflated by placing avacuum on the container. Preferably the open cell foam is shaped in the desired configuration at the time the foam is being molded or at the time it is being cut from the slab stock. For instance, the foam may be formed in a mold having the desiredrectangular configuration, for instance 3.times.3 feet.times.3 inches. Then this foam is given a brush or roll coat of a suitable adhesive and the rubberized fabric is spread thereon and adhered to the foam by the adhesive with the seams in the fabricbeing cemented together with a suitable fabric adhesive.
Polyurethane foams can be prepared by reacting an organic polyisocyanate with a hydrocarbon polyol of about 500 to 10,000 molecular weight and preferably 700 to 4,000 molecular weight in the presence of a blowing agent such as water, a lowboiling or gas generating agent or combinations of these, either with or without various polyurethane catalysts. Other useful foams are latex foam and vinyl resin foams.
These foams can be reticulated by subjecting the foam to a flame front or fire polishing to remove the thin diaphragm covering of the windows of the individual cells and cause thickening of the cell walls as the foam passes through a stateapproximating its thermoplastic or flow temperature.
The nature of the reticulated foams may more readily be understood by reference to the following examples wherein all parts are by weight unless otherwise indicated.
EXAMPLE I
One hundred thousand parts by weight of a hydroxyl terminated copolymer of butadiene and acrylonitrile of about 2,000 molecular weight where the butadiene content is approximately 85 percent and the acrylonitrile content is approximately 15percent containing 3,000 parts of water, 270 parts of dibutyl tin dilaurate, 90 parts of 2-dimethylamino-2-methyl-1-propanol and 25 parts of silicone .gamma. and 200 parts of Silicone L-520 were mixed in a suitable one-shot foam apparatus (an AdmiralFoam machine) with 35,000 parts of a commercial toluene diisocyanate (80/20 isomeric mixture) and allowed to foam in a cubic shaped mold of about 1 cubic foot to form a foam having a density of about 2 pounds per cubic foot. A specimen of this curedfoam was placed within a suitable retaining mold and the pores or cells thereof filled with a mixture of approximately 20 percent propane and 80 percent oxygen. Then the mold was closed and the propane-oxygen mixture was ignited by passing a currentfrom a 10,000-volt spark generator through an automobile spark plug projecting within the mold. The resulting explosion reticulated or fire polished the foam to give a foam bun having approximately 5 pores per inch. In other cases foams weresuccessfully reticulated containing up to 100 pores per inch. This reticulated foam had an orange color and a density of approximately 2 pounds per cubic foot, a tensile strength of approximately 12 to 14 pounds per square inch and an ultimateelongation of approximately 150 to 160 percent and a tear resistance of 5 pounds per inch.
Silicon L-520 is a blocked silicone oxyalkylene copolymer where the hydrocarbon radicals of the blocks are oxyethylene and oxypropylene containing 15 to 19 oxyethylene and 11 to 15 oxypropylene units. Silicone .gamma. is a poly oxyalkylenesilicone where the alkylene radical is propylene.
EXAMPLE II
Other foams were made with the recipe shown for Runs A to D, in Table 1:
TABLE 1 ______________________________________ Run Numbers A B C D ______________________________________ Polybutadiene diol 100 100 100 100 Water 3 3 3 3 Dibutyltin dilaurate 0.26 0.33 0.33 0.33 2-Dimethylamino-2-methyl-1- 0.44 0.440.42 0.44 propanol Silicone y 0.025 0.05 0.05 0.05 Silicone L-520 0.20 0.23 0.28 0.25 Toluene diisocyanate 38 38 38 38 (80/20 isomers) ______________________________________
The foam from Run A had relatively large cells, while the foam from Run B had cells of approximately the same average size except some smaller cells were intermixed with the larger cells. The foams of Runs C and D have very noticeable windowscovering the cells. Instead of polybutadiene diol, the polyisoprene diols can be used to make foams, too.
Other foams can be made by the one-shot method although the prepolymer or other well-known methods could be used with appropriate adjustment of the catalyst and blowing agent ratios. Also, any of the polyether or polyesters useful for makingfoams can be used, too. For instance, in Example II a polybutadiene diol having a hydroxyl content of 0.75 milliequivalents per gram was used as the resin and the ingredients were mixed and foamed according to the one-shot technique. The resultingfoams had varying cell size with noticeable windows or thin films covering the cells.
A crude methane diphenyl diisocyanate, about 60 parts per 100 parts of the polybutadiene diol, was used instead of toluene diisocyanate to make a satisfactory foam with the above polyols. Other organic polyisocyanates can be used.
Any organic polyisocyanate or mixtures of polyisocyanates may be employed in preparing the cellular polyurethane products. The amount of polyisocyanate employed should be at least sufficient to crosslink the active-hydrogen-containing polymericmaterial and to react with the water present to generate carbon dioxide gas so generated causes the liquid reaction mixture to foam and form cellular products. In general, it is preferred to use from 2 to 8 equivalents of isocyanate per mol of polymericmaterial with best results being obtained by the use of approximately 3 mols of a diisocyanate per mol of polymeric material. Representative examples of polyisocyanates which may be employed are the diisocyanates such as hexamethylene diisocyanate;paraphenylene diisocyanate; meta-phenylene diisocyanate; 4,4'-diphenylene diisocyanate; 1,5-naphthalene diisocyanate; 4,4'-diphenylene methane diisocyanate; the tolylene diisocyanates; 4,4'-diphenyl ether diisocyanate; 3,3'-dimethyl 4,4'-diphenyldiisocyanate; and 3,3'-dimethoxy 4,4'-diphenyl diisocyanate; the triisocyanates such as 4,4',4"-triphenyl methane diisocyanate; and toluene 2,4,6-triisocyanate; the tetraisocyanates such as 4,4'-dimethyldiphenyl methane 2,2',5,5'-tetraisocyanate andmixtures of polyisocyanates. Of these the liquid tolylene diisocyanates, such as 2,4-tolylene diisocyanate and 2,6-tolylene diisocyanate or mixtures thereof and toluene 2,4,6-triisocyanate are particularly preferred.
A copolymer containing approximately 75 percent butadiene and approximately 25 percent styrene and having a hydroxyl content of 0.75 milli-equivalents per gram (designated hereinafter as Resin CS-15) can be used to prepare a foam by the one-shottechnique.
The hydrocarbon diols or polyols of 2 to 5 hydroxyls useful in this invention in general are prepared by polymerizing an olefin such as a conjugated diolefin alone or in conjunction with an alpha olefin to give a polymer which is then hydroxylterminated. Representative examples of these olefins are ethylene, propylene, butylene, amylene, hexylene, styrene, acrylonitrile and related aliphatic and aromatic olefins of about two to 20 carbon atoms, with those of two to 12 being the moredesirable ones. The conjugated diolefins are represented by butadiene, isoprene, piperylene, ethyl butadiene and the other well-known conjugated diolefins having from four to 12 carbon atoms.
The polymerization of the olefins may be achieved with an alkali metal such as lithium or organo-alkali compounds and then the hydroxyl group is introduced by removal of the alkali metal with water, formaldehyde, ethylene oxide and other agentswell known to the art. It should be indicated that the degree of saturation or unsaturation can be controlled by hydrogenation.
The foams prepared in Example I, as well as the polyisoprene diol prepared foam, were reticulated according to the technique described in Example I and the resulting foams were found to be equivalent in physical characteristics to the commercialreticulated polyesterurethane foams and superior thereto in their resistance to hydrolysis and microbiological attack.
The amount of blowing agent used is controlled normally by the density desired in the finished foam. For instance, the water can vary from 0.5 to about 5 or 6 parts per hundred. The blowing agents such as the fluorinated hydrocarbons andmethylene chloride can be used in equivalent amounts to vary the foam density.
Reticulated foam is used within this specification to indicate a foam which has been fire polished to destroy the membranes or thin films joining the strands which divide contiguous cells without destroying the strands of the skeletal structure,or has been treated chemically to destroy the strands or windows.
EXAMPLE III
A block of reticulated polyester polyurethane foam obtained from the Foam Division, Scott Paper Company, as Scott Industrial Foam, 20-10 pores per inch, having the dimensions 30.times.30.times.31/2 inches, was covered with a square woven nyloncloth which previously had been coated with 50/50 toluene methyl ethyl ketone solution of a polyurethane liquid reaction mixture of 2,000 molecular weight polyethylene adipate, polypropylene adipate, 2,000 molecular weight polybutylene adipate reactedwith toluene diisocyanate (80/20 isomer mixture), to form a prepolymer and then further reacted with methylene orthodichloroaniline and mercaptobenzothiazole. The liquid reaction mixture used to precoat the cloth was also used as the adhesive betweenthe coated fabric and the foam and in seaming the coated fabric. A valve was adhered to the coated fabric. The structural component was heated in an oven at 230.degree. F. for 3 hours, prior to making the final seams, to evaporate all solvent from thefoam and adhesive.
The structural component was then attached to a vacuum pump. The panel was reduced in thickness from 31/2 inches to 3/8 inch. The structural component was then inflated with compressed air. The panel was essentially dimensionally stable as thepressure was increased from 0 to 10 p.s.i. Between 10 and 20 p.s.i. there was some increase in thickness. Thus, this degree of inflation is sufficient to give the bag the desired rigidity without destroying the foam, where p.s.i. is gauge.
EXAMPLE IV
An open celled polypropylene ether urethane foam unreticulated, having dimensions such as 12.times.2 feet.times.4 inches may be covered with an open weave nylon fabric with the seams 5 being cemented together with a polyurethane reaction mixture. Then the foam 6 covered with cloth 7 may be given a coating of a very dilute (about 5-10 percent solids) polyurethane reaction mixture to tie the cloth to the foam and also at least partly fill the interstices of the fabric. With the cloth bonded to thefoam, it is preferred that the next coat of polyurethane reaction mixture be applied in a more concentrated form, i.e. less solvent to build up an airtight covering of about 5 to 25 mils depending on pressure to which the finished container is to besubjected. A valve member 8 may be placed on the cloth prior to application of the first coat of polyurethane and thus be built into the finished container.
It should be appreciated that where the foam is so shaped (for instance, the part shown in dotted outline 10 in FIG. 1 is removed) this container could be a ladder or related structural member.
While certain representative embodiments and details have been shown for the purpose of illustrating the invention, it will be apparent to those skilled in this art that various changes and modifications may be made therein without departing fromthe spirit or scope of the invention.
* * * * * |
|
|
|
 |
|
 |
|
| |