Manufacture of naphthenic type lubricating oils |
| RE30529 |
Manufacture of naphthenic type lubricating oils
|
|
| Patent Drawings: | |
| Inventor: |
Reynolds |
| Date Issued: |
February 24, 1981 |
| Application: |
06/078,616 |
| Filed: |
September 24, 1979 |
| Inventors: |
Reynolds; Ronald W. (Wilmington, DE)
|
| Assignee: |
Sun Oil Company of Pennsylvania (Philadelphia, PA) |
| Primary Examiner: |
Levine; Herbert |
| Assistant Examiner: |
|
| Attorney Or Agent: |
Hess; J. EdwardJohnson; Donald R.Lipsitz; Paul |
| U.S. Class: |
208/111.3; 208/111.35; 208/18; 208/57; 208/92 |
| Field Of Search: |
208/18; 208/57; 208/92; 208/93 |
| International Class: |
|
| U.S Patent Documents: |
3902988; 3926786; 3929616 |
| Foreign Patent Documents: |
|
| Other References: |
|
|
| Abstract: |
A process for making naphthenic type lubricating oils from a low VI waxy crude which comprises distilling said low VI waxy crude to 500.degree. to 650.degree. F. at atmospheric pressure to separate distillable fractions therefrom, subjecting the residue to a vacuum distillation at about 25 to about 125 mm Hg absolute pressure to obtain one or more gas oil fractions, optionally hydrotreating said gas oil fractions in the presence of a Ni/Mo catalyst at 550.degree. to 650.degree. F., 0.25 to 1.0 LHSV, and 700-1500 psig, and catalytically dewaxing said distillates in the presence of a H.sup.+ form mordenite catalyst containing a Group VI or Group VIII metal at 550.degree. to 750.degree. F., 500 to 1500 psig and 0.25 to 5.0 LHSV, to obtain said naphthenic type oils having pour points of from about -60.degree. to +20.degree. F. |
| Claim: |
The invention claimed is:
1. A process for making naphthenic type lubricating oils from a low VI waxy crude .Iadd.unsuitable for solvent lubes .Iaddend.which consists of distilling said low VIwaxy crude to 500.degree. to 650.degree. F. at atmospheric pressure to separate distillable fractions therefrom, subjecting .Iadd.all of .Iaddend.the residue to a vacuum distillation at about 25 to about 125 mm Hg absolute pressure to obtain one ormore distillate fractions having an SUS at 100.degree. F. viscosity of from about 60 to about 2000, and catalytically dewaxing .[.all of.]. said .[.distillates.]. .Iadd.distillate fractions .Iaddend.in the presence of an H.sup.+ form mordenitecatalyst containing a Group VI or Group VIII metal at 550.degree. to 750.degree. F., 500 to 1500 psig and 0.25 to 5.0 LHSV to obtain said naphthenic type oils having a pour point of from about -50.degree. to +20.degree. F.
2. The process of claim 1 where the low VI waxy crude is Nigerian Medium.
3. The process of claim 1 where catalytic dewaxing is carried out in a fixed bed, trickle flow reactor.
4. The process of claim 1 where sulfur is added to the H.sup.+ mordenite catalyst.
5. A process for making naphthenic type lubricating oils .[.fom.]. .Iadd.from .Iaddend.a VI waxy crude which consists of atmospherically distilling said crude to remove wet gas, straight run gasoline, naphtha and atmospheric gas oil fractions,subjecting the residue to a vacuum distillation at about 25 to 120 mm mercury pressure absolute to obtain gas oil fractions having an SUS at 100.degree. F. viscosity of from about 60 to about 2000, hydrotreating said gas oil fractions in the presence ofa Ni/Mo catalyst at about 650.degree. F., a hydrogen pressure of about 800 psig and a LHSV of about 1.0, and catalytically dewaxing said hydrotreated gas oil fractions in the presence of an H.sup.+ form mordenite catalyst containing platinum at atemperature of about 550.degree. to about 600.degree. F., a hydrogen pressure of about 850 psig, and a LHSV of from about 0.8 to about 1.0 to obtain naphthenic type oils having a pour point of from about -60.degree. to about 20.degree. F.
6. The process of claim 5 where the low VI waxy crude is Nigerian Medium. |
| Description: |
Naphthenic lubricating oils are conventionally made from grade A or coastal, wax-free crudes by simpledistillation of the crude in the presence of caustic. Due to such simple processing they have been relatively inexpensive.
Naphthenic oils have naturally low pour points of from -50.degree. F. in low viscosity grades to +20.degree. F. in high viscosity grades. Their viscosity Index (VI) is poor, but, in many applications, this quality is secondary to costconsiderations. There are also some applications where the particular properties of naphthenic lubes (very low pour point and relatively high content of aromatic compounds) make them desirable in spite of any price advantage.
Solvent lubricating oils are made from waxy crudes. They require a complicated refining scheme and are, therefore, more expensive. VI is high and pour points of finished oils (after dewaxing) run 0 to +10.degree. F. These lubes must bemanufactured from selected waxy crudes, i.e., those with VI high enough to give at least 90-95 VI levels in the finished oils. Waxy crudes with lower VI potential are rejected for solvent lube manufacture and utilized only for fuels.
This invention is directed to a process for manufacturing relatively inexpensive naphthenic type lubes from the low VI waxy crudes unsuitable for solvent lubes and now used for gasoline and fuels. Such a process is desirable because reserves ofgrade A or coastal crudes are seriously declining and no new fields of these grades have been discovered. Thus, the process of this invention will permit crudes now going to fuels to fill this gap while saving high VI solvent lube crudes forapplications where their special qualities are required.
In essence, the process of the invention involves the steps of distilling a low VI waxy crude at atmospheric pressure up to a temperature of about 650.degree. F. to remove the distillable fraction therefrom, vacuum distilling the residue toobtain gas oil fractions and catalytically dewaxing the gas oil fractions having an SUS at 100.degree. F. viscosity of from about 60 to about 2000 to obtain the naphthenic type lubricating oil product. Optionally, prior to the catalytic dewaxing stepthe gas oil fractions may be hydrogenated if it is desired to improve color and/or remove nitrogen and sulfur compounds which is desirable for enhanced product quality or to avoid the adverse effects of sulfur and nitrogen on the dewaxing catalyst.
Reference is now made to the drawing where the process of the invention is illustrated in more detail. The crude is first taken through line 11 to a still 12 and distilled at atmospheric pressure up to a temperature of about 650.degree. F. anddistillates are sent to fuels manufacture as shown by lines 13, 14 and 15. The residual crude is taken through line 16 to still 17 and vacuum distilled at about 25 to about 125 mm of mercury pressure (absolute) to give several gas oils of desiredviscosities. The atmospheric and vacuum distillation columns may include caustic scrubbing zones to remove undesirable acids in the crude. The vacuum gas oils may next be taken through appropriate lines, shown in the FIGURE as lines 18 to 22 to anoptional hydrotreater 23 and hydrotreated to improve color and remove nitrogen and sulfur compounds. Whether or not hydrotreating will be used depends on the properties of the specific crudes used along with the desired end uses for the finished lubes. If used, the operating conditions for the hydrotreating step are:
Temperature, .degree.F.: 550.degree.-650.degree.
H.sub.2 pressure, Psig: 700-1500
LHSV: 0.25-1.0
Catalyst: Commercially available Ni-Mo
Finally, the distillates are taken through lines 24 to 28 to a dewaxer 29 where they are catalytically dewaxed to meet pour point specifications. This is accomplished by mixing the oil with hydrogen and contacting it with a catalyst at elevatedtemperature and pressure. Normal paraffins and nearly normal paraffins are preferentially cracked to gases and low boiling liquids which may be removed by distillation (not shown). Operating conditions are:
Temperature, .degree.F.: 500.degree.-750.degree.
H.sub.2 pressure, Psig: 500-1500
LHSV: 0.25-5.0
H.sub.2 recycle, SCF/bbl: 1,000-10,000
The catalyst used is an alumino-silicate of the mordenite class. It must be decationized, that is Na+ ions replaced with H+ ions, to be active for this application. A commercially available example of H+ mordenite is Norton Company's Zeolon H.A group VI or VIII metal such as platinum or palladium is added to the hydrogen mordenite to give the final catalyst. In an alternate catalyst, sulfur also may be added to the H+ mordenite by using a sulfuric acid treatment before adding the group VI orVIII metal. The sulfur addition is readily accomplished by slurrying H+ mordenite with H.sub.2 SO.sub.4 at 90.degree. C. for 5 hours. After filtration to remove excess H.sub.2 SO.sub.4 liquid, the acid laden mordenite is heated in a programmed mannerto 480.degree. C. to volatilize acid. Final catalyst contains at least 0.05 wt. % sulfur and more typically 2-4 wt. %.
The catalytic dewaxing operation is preferably carried out in a fixed bed, trickle flow reactor. High pressure and low pressure separators remove hydrogen and hydrocarbon gases from the effluent. A vacuum stripper removes products ofhydrocracking boiling lower than the feed. Severity is adjusted to meet the spedific pour point target of each distillate.
Catalytic dewaxing severity would be adjusted to give the following pour points for the particular viscosity grades from the vacuum distillation:
______________________________________ Viscosity Grade Dewaxed Pour Point (SUS @ 100.degree. F.) (F..degree.) ______________________________________ 60 -50 100 -40 500 -10 2000 +10 ______________________________________
A specific example of the type of crude for which this invention is useful is Nigerian Medium. Nigerian Medium may be contrasted with naphthenic crude and high VI waxy crude as follows:
______________________________________ Amelia A/ Zarzaitine Perkins A Nigerian (Typical High (Typical Medium VI Waxy Sol- Naphthenic (Low VI vent Lube Crude) Waxy Crude) Crude) ______________________________________ Crude Properties .degree.API 24.0 26.1 42 WT. % wax 0.3 3.0 4.0-5.0 650-1070.degree. F. Fraction Vol. % crude 36 34 22.5 WT. % wax .4-.5 8 13-15 Dewaxed satu- rates VI 20-40 75 104 ______________________________________
Nigerian Medium lacks the VI potential to make a 95 VI solvent lube, but it contains wax and, thus, conventionally would only be used for fuel manufacture. By using the process of this invention, an inexpensive lube of intermediate VI qualitymay be manufactured from Nigerian Medium crude. Other useful crudes include Trinidad Light, Garden Island Bay and Lake Washington (Louisiana Crudes), Thompson, Webster and Hawkins (Texas Crudes), which crudes contain wax and cannot by prior art methodsyield 90 VI solvent lubes.
In order to further illustrate the invention the following examples are given:
EXAMPLE 1
A sample of Nigerian Medium crude was distilled in a commercial atmospheric distillation unit containing a caustic scrubbing zone to give the following streams:
______________________________________ Approx. Stream B. Pt. (.degree.F.) Vol. % on Crude ______________________________________ Wet gas To 250.degree. 6.0 Straight run gasoline Naphtha 250.degree.-420.degree. 8.0 Atmospheric gas oil 420.degree.-520.degree. 22.0 Residue 520.degree.+ 64.0 ______________________________________
The residue was then distilled in a commercial vacuum distillation unit also containing a caustic scrubber at 25 to 120 mm of mercury pressure (absolute) to give the streams shown in Table I.
TABLE I ______________________________________ Vol % D1160 VIS Ppm Stream of Distill, .degree.F. SUS/ Sul- Pour D-1500 No. Crude 10% 90% .degree.API 100.degree. F. fur Pt. Color ______________________________________ 1 13.0 -- -- -- ---- -- -- 2 3.5 578 707 23.9 64 2000 +12 1.0 3 11.0 608 787 22.8 124 1700 +44 1.75 4 5.0 704 871 20.7 560 2400 +71 2.75 5 11.0 773 956 18.9 2000 2400 +88 4.0 6 5.0 813 1064 18.1 5000 3200 +94 6.5 Caustic 2.0 -- -- -- -- -- -- -- Sludge Vac- 13.5-- -- -- -- -- -- -- Resi- due ______________________________________
Streams 2 through 6 were then hydrotreated using a commercially available Ni-MO catalyst (American Cyanamid HDS-9 Trilobe). The hydrotreating was conducted at a reactor temperature of 650.degree. F., hydrogen pressure of 900 psig, a liquidhourly space velocity (LHSV) of 1.0, and a hydrogen recycle of 150 to 200 SCF/Bbl. After hydrotreating the sulfur content was seen to have been reduced and color was improved while pour point remained the same. The properties of the streams from thehydrotreater are shown in the following table:
______________________________________ Ppm D 1500 Pour Stream Sulfur Color Point of ______________________________________ 2 96 0.75 +12 3 225 1.25 +42 4 393 1.50 +70 5 503 2.25 +88 6 626 2.75 +94 ______________________________________
The above hydrotreated streams were then catalytically dewaxed using a commercially available mordenite catalyst in hydrogen from (Norton Zeolon H) to which had been added 0.5% by weight of platinum. The dewaxing was carried out in a fixed bedtrickle flow reactor operated at 550.degree. to 600.degree. F., a hydrogen pressure of 850 psig, liquid hourly space velocity of 0.8 to 1.0 and a hydrogen recycle of 5000 to 9000 SCF/Bbl. The following table shows the yields of naphthenic-typelubricating oil products obtained and their pour points.
______________________________________ Yield, Wt. % of Charge Product Stream C.sub.1 -C.sub.5 C.sub.5 -IBP IBP Pour Pt. .degree.F. ______________________________________ 2 3.5 4.5 92.0 -60 3 2.0 2.0 96.0 -40 4 5.0 3.0 92.0 -30 5 2.5 3.094.5 +08 6 1.5 0.5 98.0 70 ______________________________________
As can be seen from the above table, Streams 2 to 5 yield a product fully meeting the specifications for naphthenic type lubricating oils. With extremely heavy grades such as stream 6 where the SUS/100.degree. F. viscosity is 5000, the productobtained exceeds the pour point specification for the naphthenic type lubricating oils and such heavy grades from the vacuum distillation or optional hydrogenation step, rather than be subjected to catalytic dewaxing, would be used in other refineryoperations or could be dewaxed by solvent dewaxing.
* * * * * |
|
|
|
 |
|
 |
|
| |